Alkaline degreaser for iron and steel
1N123
| Features | Offers outstanding degreasing performance, low foaming, and wear resistance. |
| Application Conditions | Concentration: 40-90g/L Temperature: 40-60℃ Time: 5-20 minutes |
- 1N123
-
Pack Size: 20kg
CA-130
| Features | Can also be used as a non-silicate electrolytic degreaser. |
| Application Conditions | Concentration: 40-100g/L Temperature: 40-90℃ Time: 3-10 minutes |
- CA-130
-
Pack Size: 20kg
CA-132
| Features | Extremely high detergency and excellent aging properties. |
| Application Conditions | Concentration: 30g/L Temperature: 40-80℃ Time: 1-3 minutes |
- CA-132
-
Pack Size: 20kg
1K088
| Features | It has exremely good solubility,and any type of oil and fat can be easily removed by dipping treatment. |
| Application Conditions | Concentration: 40-60g/L Temperature: 60-80℃ Time: 5-20 minutes |
- 1K088
-
Pack Size: 20kg
Alkaline additive degreaser for iron and steel
Plus Clean
| Features | Only requires a small amount of product, which allows for a large cost savings. |
| Application Conditions | Concentration: Caustic ｓoda 10-50g/L Plus Clean A 0.5-2ml/L Plus Clean B 5-20mL/L Temperature: 40-70℃ Time: 3 minutes, or as needed |
- Plus Clean A
-
Pack Size: 18kg
- Plus Clean B
-
Pack Size: 20kg
Phosphoric acid coating remover and degreaser for iron and steel
1M115
| Features | Remove phosphate coatings and degrease simultaneously. |
| Application Conditions | Concentration: 30-60g/L Temperature: 40-60℃ Time: 5-20 minutes |
- 1M115
-
Pack Size: 20kg
Alkaline polishing debris remover
A-1911
| Features | Allows for removing solid polishing debris. |
| Application Conditions | Concentration: 40-100g/L Temperature: 40-70℃ Time: 5-15 minutes |
- A-1911
-
Pack Size: 20kg
Oil lifting agent for use in emulsified degreasing solutions
Additive 22
| Features | Allows for separating and removing oil content from an emulsified degreaser. |
| Application Conditions | Concentration: 0.5-2mL/L in emulsified degreasing solution |
- Additive 22
-
Pack Size: 17kg
Alkaline degreaser for copper and copper alloys
1P139
| Features | Offers strong degreasing capability. |
| Application Conditions | Concentration: 30-60g/L Temperature: 50-60℃ Time: 5-10 minutes |
- 1P139
-
Pack Size: 20kg
Stainless steel degreaser
1H061
| Features | Slightly alkaline liquid properties. |
| Application Conditions | Concentration: 30-70mL/L Temperature: 60-80℃ Time: 5-15 minutes |
- 1H061
-
Pack Size: 20kg
Degreaser for aluminum alloy
1N124
| Features | Neutral liquid product that maintains metallic gloss of the product. |
| Application Conditions | Concentration: 20-50mL/L Temperature: 40-60℃ Time: 3-15 minutes |
- 1N124
-
Pack Size: 18kg
Keiclean 6
| Features | Weak alkaline liquid with excellent cleansing power. |
| Application Conditions | Concentration: 10-50mL/L Temperature: room temperature up to 60℃ Time: 3-10 minutes |
- Keiclean 6
-
Pack Size: 20kg
G-0927
| Features | Neutral alkaline product with excellent degreasing and cleansing performance. |
| Application Conditions | Concentration: 5-40g/L Temperature: 40-60℃ Time: 1-5 minutes |
- G-0927
-
Pack Size: 20kg
Degreaser for zinc die cast
Keiclean 3
| Features | Weak alkaline product with excellent cleansing power. |
| Application Conditions | Concentration: 30g/L Temperature: 60-70℃ Time: 3-5 minutes |
- Keiclean 3
-
Pack Size: 20kg
Degreaser for magnesium alloy
1M108
| Features | Prevents tarnishing base materials. |
| Application Conditions | Concentration: 20-40g/L Temperature: 40-60℃ Time: 3-10 minutes |
- 1M108
-
Pack Size: 20kg
Emulsion cleanser
K-0606
| Features | Superior in degreasing,emulsion type. |
| Application Conditions | Concentration: 30-50mL/L Temperature: 20-50℃ Time: 3-20 minutes |
- K-0606
-
Pack Size: 17kg
Spray cleanser with anti-rust properties
1B011
| Features | Slightly alkaline liquid properties. |
| Application Conditions | Concentration: 10-50mL/L Temperature: 20-80℃ Time: 0.5-1 minutes |
- 1B011
-
Pack Size: 18kg
Low foam electrolytic degreaser for iron, steel, copper and copper alloys
Y-2423
| Features | Non-silicate product for excellent wastewater treatment. |
| Application Conditions |
Concentration: 20-100g/L Temperature: room temperature up to 60℃ Time: 1-5 minutes Current Density: 3-15A/d㎡ |
- Y-2423
-
Pack Size: 20kg
Non-cyanide electrolytic cleanser
CV-251
| Features | Liquid,caustic soda is added separately. |
| Application Conditions |
Concentration: CV-251 50mL/L Caustic Soda 50g/L Temperature: room temperature up to 50℃ Time: 30 seconds to 3 minutes Current Density: 5-20A/d㎡ (+)(-)PR |
- CV-251
-
Pack Size: 20kg
CV-260
| Features | Non-cyanyde anode electrolytic cleaning agent that completely removes smut,oils,and light rust from iron products. |
| Application Conditions |
Concentration: CV-260 50g/L Caustic Soda 80g/L Temperature: room temperature up to 50℃ Time: 1-4 minutes Current Density: 4-10A/d㎡ (+) |
- CV-260
-
Pack Size: 20kg
CV-261
| Features | Low chelate powdered type. |
| Application Conditions |
Concentration: 100-150g/L Temperature: room temperature up to 50℃ Time: 1-5 minutes Current Density: 5-10A/d㎡(+)PR |
- CV-261
-
Pack Size: 20kg
Alkaline rust remover for Iron Steel
RA-290
| Features | alkaline type rust remover.Both dipping and electrolysis (+) methods can be used. |
| Application Conditions |
Dipping method Concentration: RA-290 200-300g/L Temperature: Room temperture to 50℃ Time: 5-20 minutes electrolysis method Concentration: RA-290 100-150g/L Temperature: 60-90℃ Time: 5-20 minutes Electrode: Carbon,steel Current Density: 6-10A/d㎡ (+) |
- RA-290
-
Pack Size: 20kg