Products
Brightener for zincate baths
【For Barrel Plating】Hyperzinc 300
| Features | Excellent productivity -- obtain desired film thickness in short amount of time. Glossy finish will persist even after baking process. Allows for working with iron anodes. The concentrated agent for greater cost savings. |
| Application Conditions | Zinc: 8-15g/L Caustic soda: 110-150g/L 300A or S: 3-5mL/L 300B or R: 0.5-3mL/L Hypersoft: 7-15mL/L Temperature: 20-35℃ Current Density: 0.2-2A/d㎡ |
- Hyperzinc 300A or S
-
Pack Size: 20kg
- Hyperzinc 300B or R
-
Pack Size: 20kg
【For Rack Plating】Hyperzinc 9500
| Features | Good chemistry with trivalent chromium coatings and stable corrosion resistance. Highly uniform electrodeposition and throwing power. Accommodates a wide range of bath compositions, temperatures and quantities of electricity. The concentrated agent for greater cost savings. |
| Application Conditions | Zinc: 8-15g/L Caustic soda: 110-150g/L 9500A: 4-6mL/L 9500B: 0.2-1mL/L Hypersoft: 7-15mL/L Temperature: 20-30℃ Current Density: 2-5A/d㎡ |
- Hyperzinc 9500A
-
Pack Size: 18kg
- Hyperzinc 9500B
-
Pack Size: 18kg
【For Rack Plating】Hyperzinc 9000
| Features | Good chemistry with trivalent chromium coatings and stable corrosion resistance. Excellent uniformity of electrodeposition and throwing power. Obtain desired film thickness in short amount of time. Allows for working with iron anodes. Good plating phigical properties and well-suited for items that are bent after plating. |
| Application Conditions | Zinc: 8-15g/L Caustic soda: 110-150g/L 9000A: 10-15mL/L 9000BS: 0.2-2mL/L Hypersoft: 7-15mL/L Temperature: 20-30℃ Current Density: 2-5A/d㎡ |
- Hyperzinc 9000A
-
Pack Size: 20kg
- Hyperzinc 9000BS
-
Pack Size: 18kg
【For Rack Plating】Hyperzinc 9000FG
| Features | Highly uniform electrodeposition and high-quality glossiness create a clear and attractive appearance. Good chemistry with trivalent chromium coatings and stable corrosion resistance. Good plating phigical properties and well-suited for items that are bent after plating. |
| Application Conditions | Zinc: 8-15g/L Caustic soda: 110-150g/L 9000F: 10-15mL/L 9000G: 0.2-1mL/ Hypersoft: 7-15mL/L Temperature: 20-30℃ Current Density: 2-5A/d㎡ |
- Hyperzinc 9000F
-
Pack Size: 20kg
- Hyperzinc 9000G
-
Pack Size: 20kg
【For Barrel Plating】Hyperzinc 7900
| Features | Good chemistry with trivalent chromium coatings and stable corrosion resistance. Highly uniform electrodeposition and throwing power. Allows for working with iron anodes. Good plating phigical properties and well-suited for items that are bent after plating. |
| Application Conditions | Zinc: 8-15g/L Caustic soda: 110-150g/L 7900A: 10-15mL/L 7900BS: 0.5-2mL/L Hypersoft: 7-15mL/L Temperature: 20-30℃ Current Density: 0.2-2A/d㎡ |
- Hyperzinc 7900A
-
Pack Size: 20kg
- Hyperzinc 7900BS
-
Pack Size: 18kg
【For Barrel Plating】Hyperzinc 7900L
| Features | Highly uniform electrodeposition and high-quality glossiness create a clear and attractive appearance. Suitable for large quantities of overlapping and small objects Allows for working with iron anodes. |
| Application Conditions | Zinc: 8-15g/L Caustic soda: 100-150g/L 7900LM: 5-10mL/L 7900L: replenishment only 3L085: 0-0.5mL/L Hypersoft: 7-15mL/L Temperature: 20-30℃ Current Density: 0.2-2A/d㎡ |
- Hyperzinc 7900LM
-
Pack Size: 18kg
- Hyperzinc 7900L
-
Pack Size: 18kg
- 3L085
-
Pack Size: 18kg
Brightener for acidic ammonium chloride baths
3M091
| Features | Wide current density range for gloss with good leveling performance. High clouding point allows for use in high temperature plating applications. Rapid electrodeposition makes it ideal for mass plating for small items. Allows for plating on cast metal, sintered metal and heat-treated steel. |
| Application Conditions | Zinc: 15-30g/L Total chlorine: 130-160g/L 3M091A: 20-40mL/L 3M091B: 0.2-0.5mL/L Temperature: 18-50℃ Current Density: 0.5-6A/d㎡ pH: 5.0-6.3 |
- 3M091A
-
Pack Size: 20kg
- 3M091B
-
Pack Size: 20kg
Acid bath brightener
Acid Zinc 6600
| Features | Used for ammonium and potassium mixed bath. High clouding point allows for use in high temperature plating applications. Allows for achieving high quality gloss at a wide current density range. |
| Application Conditions | (For use in ammonium and potassium mixed bath) Zinc: 25-40g/L Ammonium chloride: 15-50g/L Potassium chloride: 180-240g/L 6600AS: 20-40mL/L 6600BW: 0.2-0.6mL/L Temperature: 20-40℃ Current Density: 0.5-5A/d㎡ Ph: 5.0-5.6 |
- 6600AS
-
Pack Size: 18kg
- 6600BW
-
Pack Size: 18kg
Cyanide bath brightener
【For Rack Plating】5050
| Features | Can be used in low, medium, and high cyanide baths. Strong gloss equivalent to that of a zincate bath or an acidic bath is obtained. |
| Application Conditions | (Medium cyanide bath) Zinc: 16-22g/L Sodium cyanide: 30-50g/L Caustic soda: 60-70g/L 5050: 2-3mL/L Temperature: 15-35℃ Current Density: 0.5-5A/d㎡ |
- 5050
-
Pack Size: 20kg
【For Rack Plating】5600
| Features | Can be used in low, medium, and high cyanide baths. High burn-in prevention allows for working at high currents. Wide glossy areas allows for easy management. Achieve a silvery-white exterior; chromate enhances the intensity of colors. |
| Application Conditions | (Medium cyanide bath) Zinc: 16-22g/L Sodium cyanide: 30-50g/L Caustic soda: 60-70g/L 5600: 2-3mL/L Temperature: 15-35℃ Current Density: 0.5-5A/d㎡ |
- 5600
-
Pack Size: 18kg
【For Rack Plating】J-1114
| Features | Can be used in low, medium, and high cyanide baths. High curent work is possible due to the strong anti-burning power. |
| Application Conditions | (Medium cyanide bath) Zinc: 16-22g/L Sodium cyanide: 30-50g/L Caustic soda: 60-70g/L J-1114: 2-3mL/L Temperature: 15-40℃ Current Density: 0.5-5A/d㎡ |
- J-1114
-
Pack Size: 20kg
【For Barrel Plating】31
| Features | Can be used in low, medium, and high cyanide baths. Good solubility allows for adding without further dilution. Wide glossy areas allows for easy management. Achieve a silvery-white exterior; chromate enhances the intensity of colors. |
| Application Conditions | (Medium cyanide bath) Zinc: 16-22g/L Sodium cyanide: 30-50g/L Caustic soda: 60-70g/L 31: 2-3mL/L Temperature: 15-35℃ Current Density: 0.1-5A/d㎡ |
- 31
-
Pack Size: 20kg
【For Barrel Plating】33
| Features | Can be used in low, medium, and high cyanide baths. Because of its good properties,it exhibits good performance even in low M ratio baths. |
| Application Conditions | (Medium cyanide bath) Zinc: 16-22g/L Sodium cyanide: 30-50g/L Caustic soda: 60-70g/L 33: 1-3mL/L Temperature: 15-35℃ Current Density: 0.1-3A/d㎡ |
- 33
-
Pack Size: 20kg