Gloss Agent and Trivalent Chromium Conversion Coating Agents for zinc alloy plate

  • Stronzinc line of zinc-iron alloy plate brightener
  • Trivalent chromium conversion coating agent for use in zinc-iron alloy plating
  • Stron Ni Zinc line of zinc-nickel alloy plate brightener
  • Trivalent chromium conversion coating agents for zinc-nickel alloy plating
Stronzinc line of zinc-iron alloy plate brightener

Zincate formulation gloss agent for zinc-iron alloys offers outstanding corrosion resistance.
*Please refer to each product catalog for details.

【For Barrel】Stronzinc ZF-100
Features Exhibited 3-5 times the corrosion resistance of zinc plating in saline water spray tests.
Achieve uniformity of alloy content on convex and concave surfaces and stable corrosion resistance.
【For Barrel】Stronzinc ZF-102
Features Product is more effective at treating wastewater than conventional baths.
Good chemistry with trivalent chromium coating agents and stable corrosion resistance.
【For Rack】Stronzinc ZF-105
Features Exhibited 3-5 times the corrosion resistance of zinc plating in saline water spray tests.
Achieve uniformity of alloy content on convex and concave surfaces and stable corrosion resistance.
【For Rack】Stronzinc ZF-107
Features Product is more effective at treating wastewater than conventional baths.
Good chemistry with trivalent chromium coating agents and stable corrosion resistance.

 Back to Top

Trivalent chromium conversion coating agent for use in zinc-iron alloy plating

Does not contain hexavalent chromium. Product can be used for post-processing of existing zinc-iron alloy plated materials.
*Please refer to each product catalog for details.

Tryner TRF-930
Exterior appearance White to pale yellow
Features Excellent corrosion resistance persists even after secondary processing.
Tryner TRF-966
Exterior appearance Black
Features Obtain a deep black appearance.

 Back to Top

Stron Ni Zinc line of zinc-nickel alloy plate brightener

Brightener for use in zinc-nickel alloys offers outstanding heat and corrosion resistance.
*Please refer to each product catalog for details.

【For Rack and Barrel】Stron Ni Zinc ZN-202
Nickel eutectoid ratio of plating film 5-10%
Features Ideal for plating which emphasizes secondary processing since the nickel eutectoid ratio is low.
【For Rack and Barrel】 Hi-Ni-Zn ZN-204J
Nickel eutectoid ratio of plating film 13-18%
Features Achieve stable plating with a high nickel eutectoid ratio.
【For Rack】Strontium-nickel-zinc ZN-208
Nickel eutectoid ratio of plating film 9-18% per formulation
Features Supports a wide range of nickel eutectoid ratio. Allows for achieving a higher bath temperature than traditional products and manufacturing at a higher current efficiency.
【For Barrel】Stron Ni Zinc ZN-208K
Nickel eutectoid ratio of plating film 10-18%
Features Supports a wide range of nickel eutectoid ratio. Allows for achieving a higher bath temperature than traditional products and manufacturing at a higher current efficiency.
【For Rack and Barrel】Acid Ni-Zn AZN-6900
Nickel eutectoid ratio of plating film 13-18%
Features Higher current efficiency in acid baths than in alkaline baths, allowing for shorter plating time.

 Back to Top

Trivalent chromium conversion coating agents for zinc-nickel alloy plating

Does not contain hexavalent chromium. Product can be used for post-processing of existing zinc-nickel alloy plated materials.
*Please refer to each product catalog for details.

Tryner TRN-988
Exterior appearance Blue to pale yellow
Features Uniform external appearance. Maintains excellent corrosion resistance even after secondary processing.
5P043
Exterior appearance White to pale yellow
Features Corrosion resistance remains stable even after long-term operations.
5W115
Exterior appearance Black
Features Achieve a blackish gloss in substrates with a nickel eutectoid ratio of 13% or greater.