Parting Agents

  • Alkaline-based tin and solder plating parting agent for use on iron and copper
  • Copper and solder plating parting agent for use on stainless steel
  • Tin alloy plating parting agent for use on Alloy 42
  • Tin alloy plating parting agent for use on copper alloys
  • Acid coating parting agent for aluminum surfaces
  • Alkaline coating parting agent for use on iron, stainless steel and magnesium
  • Nitrided titanium and carbonized titanium coating parting agent for use on iron, stainless steel and carbide
  • Chromium nitride coating electrolytic parting agent for use on iron and stainless steel
  • Electrolytic parting agent for titanium nitride aluminide coatings on iron and steel.
Alkaline-based tin and solder plating parting agent for use on iron and copper
SD-509
Features Allows for parting without penetrating the underlying material.
Application Conditions Concentration: SD-509A  180g/L
Caustic soda  70g/L
Temperature: 70-90℃
Time: as needed

Product Details

SD-509A

Pack Size: 20kg

  • N
SD-509B

Pack Size: 20kg

  • N

 Back to Top

Copper and solder plating parting agent for use on stainless steel
SD-576T
Features Allows for excellent parting at room temperature.
Application Conditions Concentration: undiluted
Temperature: room temperature (20-30℃)
Time: as needed

Product Details

SD-576T

Pack Size: 20kg

  • N

 Back to Top

Tin alloy plating parting agent for use on Alloy 42
6M152
Features Ideal for parting of lead-free tin alloy plating.
Application Conditions Concentration: 6M152A undiluted solution
Temperature: 45-55℃
Time: 1-5 minutes

Product Details

6M152A

Pack Size: 20kg

  • N
6M152B

Pack Size: 25kg

  • N

 Back to Top

Tin alloy plating parting agent for use on copper alloys
6M153
Features Ideal for parting of lead-free tin alloy plating.
Application Conditions Concentration: undiluted
Temperature: 20-25℃
Time: 3-10 minutes

Product Details

6M153

Pack Size: 20kg

  • N

 Back to Top

Acid coating parting agent for aluminum surfaces
6L146
Features Ideal for parting of electrodeposition coatings on anodized aluminum.
Application Conditions Concentration: 6L146M undiluted solution
Temperature: 45-55℃
Time: 5-60 minutes

Product Details

6L146M

Pack Size: 20kg

6L146H

Pack Size: 20kg

6L146T

Pack Size: 16kg

 Back to Top

Alkaline coating parting agent for use on iron, stainless steel and magnesium
6Y194
Features Chlorine-free agent that will not penetrate the underlying material.
Application Conditions Concentration: 6Y194M undiluted solution
Temperature: 70-80℃
Time: 3-60 minutes

Product Details

6Y194M

Pack Size: 20kg

  • N
6Y194T

Pack Size: 18kg

 Back to Top

Nitrided titanium and carbonized titanium coating parting agent for use on iron, stainless steel and carbide
Titanic 94
Features Allows for easy parting without penetrating the underlying material.
Application Conditions If base material is iron or stainless steel:
Concentration: Titanic 94A  500mL/L
Titanic 94B  100-200mL/L
Temperature: 25-40℃
Time: as needed
---------------------
If base material is a hard metal (carbide):
Concentration: Titanic 94A  500mL/L
Titanic 94B  100mL/L
Titanic 94C  400mL/L
Temperature: 25-30℃
Time: as needed

Product Details

Titanic 94A

Pack Size: 20kg, 1kg

  • N
Titanic 94B

Pack Size: 20kg, 1kg

Titanic 94C

Pack Size: 20kg, 1kg

  • N

 Back to Top

Chromium nitride coating electrolytic parting agent for use on iron and stainless steel
6K120
Features Cathode electrolysis allows for rapid parting.
Application Conditions Concentration: undiluted
Temperature: 20-30℃
Time: 3-30 minutes
Current Density: 5-10A/d㎡

Product Details

6K120

Pack Size: 20kg

  • N

 Back to Top

Electrolytic parting agent for titanium nitride aluminide coatings on iron and steel.
6N164
Features Allows for parting without penetrating the underlying material.
Application Conditions Concentration: undiluted
Temperature: 0-30℃
Time: as needed
Current Density: 2A/d㎡

Product Details

6N164

Pack Size: 20kg

  • N